Weld defects/imperfections in welds - lack of sidewall and inter-run fusion

Lack Of Sidewall Fusion Reactor
See Full List On Marinewiki.org

Which is the best destructive test for showing lack of side-wall fusion in a 25mm thick butt weld? Favourite answer. Weldments (Welded Joints) The most commonly occurring defects in welded joints are porosity, slag inclusions, lack of side-wall fusion, lack of inter-run fusion, lack of root penetration, undercutting, and longitudinal or transverse cracks. With the exception of single gas pores all the defects listed are usually well detectable by ultrasonics. Shaderlight plugin. The incomplete sidewall fusion was caused by insufficient input energy and higher deposited filler amount, while the instable welding process was the main reason to result in pores.

Pocanonly 4 years ago BS EN ISO 6520-1, Lack of Fusion, Lack of Penetration Lack of fusion is lack of union between the weld metal and the parent metal or between the successive layers of weld metal. Types of lack of fusion: Lack of sidewall fusion. Sidewall lack of fusion occurs when the weld metal does not fuse in to the side of the weld groove, leaving a smooth, planar discontinuity along the edge of the weld groove. Logitech drivefx axial feedback wheel. Doubling is a phenomenon that can occur when.

Demagnetising a pipe

This article describes the characteristic features and principal causes of lack of sidewall and inter-run fusion. General guidelines on best practice are given so that welders can minimise the risk of imperfections during fabrication.
Identification
Lack of fusion imperfections can occur when the weld metal fails

to fuse completely with the sidewall of the joint (Fig. 1)
to penetrate adequately the previous weld bead (Fig. 2).

Fig. 1. Lack of side wall fusion

Fig. 2. Lack of inter-run fusion

Causes
The principal causes are too narrow a joint preparation, incorrect welding parameter settings, poor welder technique and magnetic arc blow. Insufficient cleaning of oily or scaled surfaces can also contribute to lack of fusion. These types of imperfection are more likely to happen when welding in the vertical position.
Joint preparation
Too narrow a joint preparation often causes the arc to be attracted to one of the side walls causing lack of side wall fusion on the other side of the joint or inadequate penetration into the previously deposited weld bead. Too great an arc length may also increase the risk of preferential melting along one side of the joint and cause shallow penetration. In addition, a narrow joint preparation may prevent adequate access into the joint. For example, this happens in MMA welding when using a large diameter electrode, or in MIG welding where an allowance should be made for the size of the nozzle.
Welding parameters
It is important to use a sufficiently high current for the arc to penetrate into the joint sidewall. Consequently, too high a welding speed for the welding current will increase the risk of these imperfections. However, too high a current or too low a welding speed will cause weld pool flooding ahead of the arc resulting in poor or non-uniform penetration.
Welder technique
Poor welder technique such as incorrect angle or manipulation of the electrode/welding gun, will prevent adequate fusion of the joint sidewall. Weaving, especially dwelling at the joint sidewall, will enable the weld pool to wash into the parent metal, greatly improving sidewall fusion. It should be noted that the amount of weaving may be restricted by the welding procedure specification limiting the arc energy input, particularly when welding alloy or high notch toughness steels.
Magnetic arc blow
When welding ferromagnetic steels lack of fusion imperfections can be caused through uncontrolled deflection of the arc, usually termed arc blow. Arc deflection can be caused by distortion of the magnetic field produced by the arc current (Fig. 3), through:

Lack Of Sidewall Fusion Reactor

residual magnetism in the material through using magnets for handling
earth's magnetic field, for example in pipeline welding

The effect of welding past the current return cable which is bolted to the centre of the place is shown in Fig. 4. The interaction of the magnetic field surrounding the arc and that generated by the current flow in the plate to the current return cable is sufficient to deflect the weld bead. Distortion of the arc current magnetic field can be minimised by positioning the current return so that welding is always towards or away from the clamp and, in MMA welding, by using AC instead of DC. Often the only effective means is to demagnetise the steel before welding.

Fig. 3. Interaction of magnetic forces causing arc deflection

Fig. 4. Weld bead deflection in DC MMA welding caused by welding past the current return connection

See Full List On Marinewiki.org

Best practice in prevention
The following fabrication techniques can be used to prevent formation of lack of sidewall fusion imperfections:

select welding parameters (high current level, short arc length, not too high a welding speed) to promote penetration into the joint side wall without causing flooding
ensure the electrode/gun angle and manipulation technique will give adequate side wall fusion
use weaving and dwell to improve side wall fusion providing there are no heat input restrictions
if arc blow occurs, reposition the current return, use AC (in MMA welding) or demagnetise the steel

Acceptance standards
The limits for incomplete fusion imperfections in arc welded joints in steel are specified in BS EN ISO 5817 for the three quality levels (see Table). These types of imperfection are not permitted for Quality Level B (stringent) and C (intermediate). For Quality level D (moderate) they are only permitted providing they are intermittent and not surface breaking.
For arc welded joints in aluminium, long imperfections are not permitted for all three quality levels. However, for quality levels C and D, short imperfections are permitted but the total length of the imperfections is limited depending on the butt weld or the fillet weld throat thickness.